CABELEC® XS6132
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rhNqCo_CABELEC-XS6132.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® XS6132 is an electrically conductive compound based on conductive carbon black dispersed in a modified high density polyethylene resin. Its electrical and mechanical properties are permanent and are not dependent on atmospheric conditions. CABELEC® XS6132 has been specially designed for transport, packaging and product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosive powders, pigments and dangerous liquids. Typical applications for XS6132 are jerricans, drums and other containers for the transport of dangerous goods which are required to meet strict safety requirements in a series of national and international regulations. XS6132 is also recommended for automotive applications, for example, in conductive blow moulded fuel inlets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.05 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 190°C/10.0 kg | 0.60 | g/10 min | |
| 190°C/21.6 kg | 3.6 | g/10 min | |
| Molding Shrinkage - Flow 3 | 2.5 to 3.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 4(Shore D, 15 sec) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5 | ISO 527-2 | ||
| Yield, Compression Molded | 20.6 | MPa | |
| Break, Compression Molded | 27.4 | MPa | |
| Tensile Strain 6(Break, Compression Molded) | 920 | % | ISO 527-2 |
| Flexural Modulus 7 | 838 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 8(23°C) | 65 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9(1.8 MPa, Unannealed) | 41.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 10 | 126 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | 2.1E+2 | ohms | Internal Method |
| Volume Resistivity 12 | 63 | ohms·cm | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 230 | °C | |
| Cylinder Zone 2 Temp. | 190 to 230 | °C | |
| Cylinder Zone 3 Temp. | 190 to 230 | °C | |
| Cylinder Zone 4 Temp. | 190 to 230 | °C | |
| Cylinder Zone 5 Temp. | 190 to 230 | °C | |
| Melt Temperature | < 250 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E047 |
| 4 . | CTM E030 |
| 5 . | CTM E041 |
| 6 . | CTM E041 |
| 7 . | CTM E040A |
| 8 . | CTM E044A |
| 9 . | CTM E038 |
| 10 . | CTM E039 |
| 11 . | CTM E042E |
| 12 . | CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP1B20 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| VECTRA® MT1335 | Celanese Corporation | LCP | VECTRA® |
| HiFill® PA6/6 GF43 IM L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| HIFOR Xtreme® SC74869 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| ULTEM™ ATX200R resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |