Makrolon® Solid Sheet AR
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® Solid Sheet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rhMUes_MakrolonSolidSheetAR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Makrolon® AR sheet is an abrasion and enhanced UV resistant polycarbonate sheet that offers glasslike hardness coupled with the impact strength of standard polycarbonate. Additionally, Makrolon® AR offers on both surfaces enhanced resistance against yellowing and hazing for an extended service life in high profile architectural glazing. Makrolon® AR has a 10-years warranty against breakage and 5-years warranty against delamination and weathering. Applications: Typical applications for Makrolon® AR sheet include transparent sound barriers, school and hospital shelter glazing. Makrolon® AR is also used extensively in correctional and psychiatric facilities. Additionally, the product performs well for view windows and machine guards in harsh chemical environments. Due to its scratch-resistant coating, Makrolon® AR cannot be formed like other Makrolon® sheets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | > 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2350 | MPa | ISO 178 |
| Flexural Stress 2 | 90.0 | MPa | ISO 178 |
| Wear resistance- Delta Haze | |||
| -- 3 | 1 - 4 | % | ASTM D1044 |
| -- 4 | 4 - 9 | % | ANSI Z26.1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C, Partial Break) | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact 6(23°C, Partial Break) | 90 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 128 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.20 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| > 1.5 mm, ALL | HB | UL 94 | |
| 0.8 to 1.4mm, ALL | V-2 | UL 94 | |
| > 10.0 mm, Clear 8099 | V-0 | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index 7 | 1.587 | ISO 489 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 100 cycles, 500 g, CS-10F Wheel |
| 4 . | 500 cycles, 500 g, CS-10F Wheel |
| 5 . | 3 mm |
| 6 . | 3.2 mm |
| 7 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PS 500/2.2 S85-EMPERA116 | ALBIS PLASTIC GmbH | PS (GPPS) | ALCOM® PS |
| CP PRYME® Acetal AC100-27 | Chase Plastics Services Inc. | Acetal (POM) Copolymer | CP PRYME® Acetal |
| HiFill® PP GF/M40 CC NAT | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| ICORENE® N1003 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| Sarlink® TPE ML-1650N NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |