Infino XK-2307
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rhEHuE_Infino-XK-2307.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino XK-2307 is a Polyphenylene Sulfide (PPS) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/5.0 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.10 | % | |
| Across Flow : 3.20 mm | 0.30 | % | |
| Water Absorption | |||
| Equilibrium, 23°C | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 83.0 | MPa | ASTM D638 |
| Yield | 84.0 | MPa | ISO 527-2/5 |
| Flexural Modulus 2 | 18000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength 3 | |||
| -- | 120 | MPa | ASTM D790 |
| -- | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | 3.9 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 44 | J/m | ASTM D256 |
| 23°C 5 | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | > 270 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | > 270 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 2.00 to 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 290 to 300 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Nozzle Temperature | 320 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Injection Pressure | 49.0 to 127 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | Thickness: 4 mm |
| 5 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech CS9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC+ABS | Sup-tech |
| XYRON™ AT610 | Asahi Kasei Chemicals Corporation | Nylon+PPE | XYRON™ |
| ALCUDIA® EBA CA-3230B | REPSOL | EBA | ALCUDIA® EBA |
| Andur 93-AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Sylvin 9715-70 Grey 9486 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |