PALDUR® R 15 GK 20

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	pal plast GmbH
Trademark:	PALDUR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rgxpC3_PALDUR-R-15-GK-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALDUR®R 15 GK 20 is a polybutene terephthalate (PBT) product containing 20% glass beads. It can be processed by injection molding and is available in Europe. Typical application areas are: engineering/industrial accessories. Features include: flame retardant/rated flame anti-warping beautiful

General Information
Filler / Reinforcement	Glass beads, 20% filler by weight
Features	Low warpage Excellent appearance
Uses	Engineering accessories
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.45	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.38	%	ISO 62
Equilibrium, 23°C, 50% RH	14	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3500	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	50.5	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	5.0	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	189	°C	ISO 306/B50
Melting Temperature (DSC)	225	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	25.0	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3300 to 3700 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 48 to 53 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 4 to 6 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 3 to 5 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 187 to 190 °CDensity, ISO 1183: 1.44 to 1.46 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3300 to 3700 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 48 to 53 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 4 to 6 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 3 to 5 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 187 to 190 °CDensity, ISO 1183: 1.44 to 1.46 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.12 to 0.15 %

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X4195	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Tool-A-Thane UT-25	Urethane Tooling & Engineering Corp	PUR, Unspecified	Tool-A-Thane
Xuchuan XWB-355	Xuchuan Chemical (Suzhou) Co., Ltd	PUR, Unspecified	Xuchuan
NuSil MED-4135	NuSil Technology	Rubber	NuSil
LubriOne™ AT-000/05T 2S	PolyOne Corporation	Acetal (POM) Copolymer	LubriOne™