Nypol® PA A3 G13 NTLA010 NR406
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rguhi0_Nypol-PA-A3-G13-NTLA010-NR406.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 13% fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.23 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.7 | -- | % | ASTM D570 |
| Ash Content | 11 to 15 | -- | % | ASTM D2584 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ASTM D256 | |||
| -30°C | 30.0 | 40.0 | kJ/m² | |
| 23°C | 35.0 | 75.0 | kJ/m² |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 121 | 83.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4800 | 2700 | MPa | ASTM D790 |
| Flexural Strength | 165 | 115 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 4.5 | 6.0 | kJ/m² | |
| Notched Izod Impact (Area) | ASTM D256 | |||
| -30°C | 4.00 | 4.00 | kJ/m² | |
| 23°C | 4.50 | 6.00 | kJ/m² | |
| Unnotched Izod Impact | ASTM D256 | |||
| -30°C | 35 | 30 | J/m | |
| 23°C | 40 | 55 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 258 | -- | °C | |
| 1.8 MPa, Unannealed | 242 | -- | °C | |
| Vicat Softening Temperature | 257 | -- | °C | ISO 306/B |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| CLTE | ASTM E831 | |||
| Flow : 23 to 55°C | 4.2E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.7E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Electric Strength (2.00 mm) | 25 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 3.90 | -- | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.013 | -- | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime ABS ST80 | Primex Plastics Corporation | ASA+ABS | Prime ABS |
| SILVER® SA-5202 | Guangdong Silver Age Sci & Tech. Co., Ltd | TPE | SILVER® |
| SUNFROST® KD80MA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Flontech® FT-STST50-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HiFill® PA6 GF15 IM1 | Techmer Engineered Solutions | Nylon 6 | HiFill® |