Rilsan® MB 3750
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rgi6H8_Rilsan-MB-3750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan® MB 3750 is a Polyamide 11 (Nylon 11) product. It can be processed by extrusion, film extrusion, injection molding, profile extrusion, or sheet extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1040 | 1040 | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | |||
| Saturation | 2.7 | -- | % | |
| Equilibrium | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 1660 | 1530 | MPa | ISO 527-2 3 |
| Tensile Stress (Yield) | 62.0 | 54.0 | MPa | ISO 527-2 4 |
| Tensile Strain (Yield) | 6.0 | 6.0 | % | ISO 527-2 5 |
| Nominal strain at break | > 50 | > 50 | % | ISO 527-2 6 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength (-30°C) | 11.0 | 13.0 | kJ/m² | ISO 179/1eA 7 |
| Charpy impact strength | ISO 179/1eU 8 | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Puncture energy (-30°C) | -- | 100 | J | ISO 6603-2 9 |
| Puncture - maximum force (-30°C) | -- | 6500 | N | ISO 6603-2 10 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 11 | |||
| 0.45 MPa | 64.0 | -- | °C | |
| 1.8 MPa | 59.0 | -- | °C | |
| Vicat Softening Temperature (50°C/h, B (50N)) | 67.0 | -- | °C | ISO 306 12 |
| Melting Temperature 13 | 183 | -- | °C | ISO 11357-3 14 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | 10 °C/min |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA HDPE 1107 E | MBA Polymers | HDPE | MBA HDPE |
| Moplen EP300U | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Akulon® F132-C1 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Kingfa PP-R200 | Kingfa | PP, Unspecified | Kingfa |
| LUVOCOM® 1301-8291 | Lehmann & Voss & Co. | PPS | LUVOCOM® |