Durethan® BKV 140 H2.0 DUS008 900051
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rgE2di_Durethan-BKV-140-H2-0-DUS008-900051.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.46 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | -- | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 180 | -- | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | -- | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 10700 | -- | MPa | ISO 178/A |
| Flexural Stress 2(23°C) | 290 | -- | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 3(23°C) | 4.0 | -- | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66-HI, GHR, 14-110, GF40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 20 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 85 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 4 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ SX 218 V50 BLACK 38N-K | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| TECHNYL® A 218G V33 BLACK 41N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Fainplast PVC FK 0879 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Petlon Prime A1-G25-00-NT | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |
| Zytel® ST801AW NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |