TEPCON® M320
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | TEPCON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rfFgfG_TEPCON-M320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard, High Fluidity, High Cycle |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 63.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 28 | % | ISO 527-2 |
| Flexural Modulus | 2550 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.1 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| CLTE | Internal Method | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (3.00 mm) | 19 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ CL2250 | PolyOne Corporation | TPE | Versaflex™ |
| Nypol® PA C3 T30 NTLA010 NS304 | Petropol Industry and Trade of Polymers LTDA | Nylon 66/6 | Nypol® PA |
| Favorite LL515 | Favorite Plastics | LDPE+LLDPE | Favorite |
| DuraSurf™ 2001 DuraJet | Crown Plastics | UHMWPE | DuraSurf™ |
| ALCOM® PC 740/4 UV RD1472-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |