LNP™ LUBRICOMP™ SX93441D compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | reLWxm_LNP-LUBRICOMP-SX93441D-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP SX93441D is a compound based on Nylon 12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound PDX-S-93441 Product reorder name: SX93441D |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | |
| -- | 1.19 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.90 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5410 | MPa | ASTM D638 |
| -- | 5420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 93.0 | MPa | ASTM D638 |
| Yield | 92.0 | MPa | ISO 527-2/5 |
| Break 3 | 86.0 | MPa | ASTM D638 |
| Break | 91.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.9 | % | ASTM D638 |
| Yield | 4.9 | % | ISO 527-2/5 |
| Break 5 | 6.1 | % | ASTM D638 |
| Break | 6.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4480 | MPa | ASTM D790 |
| -- 7 | 4720 | MPa | ISO 178 |
| Flexural Stress | 136 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.49 | ||
| vs. Itself - Static | 0.48 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 7.45 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 51.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 870 | J/m | ASTM D4812 |
| 23°C 9 | 58 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 16.0 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 175 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 170 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 146 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIF5166 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| WINTEC™ WFX6 | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| Norprene A60G | Saint Gobain - Norton | TPE | Norprene |
| LEXAN™ 1278R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Hifax TRC 770P G01 BK MEX | LyondellBasell Industries | TPO (POE) | Hifax |