HiFill® PA6/12 CF30 BK
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rdZgPq_HiFill-PA6-12-CF30-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PA6/12 CF30 BK is a Polyamide 612 (Nylon 612) product filled with 30% carbon fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 200 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 15900 | MPa | ASTM D790 |
| Flexural Strength | 303 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 221 | °C | |
| 1.8 MPa, Unannealed | 216 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| TPCI # | 9814104 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 to 104 | °C | |
| Drying Time | 2.0 to 16 | hr | |
| Rear Temperature | 271 to 282 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Nozzle Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 271 to 282 | °C | |
| Mold Temperature | 54.4 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A ECP3808 339 NER | Radici Plastics | Nylon 66 | Radilon® |
| VENELENE® 8407APUV | Poliolefinas Internacionales, C.A. (Polinter) | MDPE | VENELENE® |
| ULTEM™ 2212EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| DOW™ LLDPE GRSN-9820 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Bakelite® PF 7596 | Hexion Inc. | Phenolic | Bakelite® |