Retpol® 9028
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rcl8Ty_Retpol-9028.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Retpol 9028 is a medium to high flow flame retardant, talc reinforced homopolymer polypropylene compound. It has been developed to meet the requirements of UL 94 V-2 flammability rating and the AS/NZS 60695.2.12 requirement for 960°C glow-wire. The talc filler reduces shrinkage and imparts higher rigidity to moulded components. The flame retardant system is based on halogenated hydrocarbons with an antimony trioxide synergist. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 to 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 33.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 1780 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact | 680 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 180 to 225 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) FABS 30 GB | A. Schulman Europe | ABS | POLYMAN® |
| Tenac™-C 7520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Kumho SSBR SOL-5220M | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| Lumiplas® LD7701FD | LG Chem Ltd. | PC | Lumiplas® |
| Sylvin 3290-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |