HiFill® PC / PET 2230
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rcNAii_HiFill-PC-PET-2230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PC / PET 2230 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/2.16 kg | 6.5 | g/10 min | |
| 300°C/1.2 kg | 14 | g/10 min | |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 238 to 266 | °C | |
| Middle Temperature | 238 to 266 | °C | |
| Front Temperature | 238 to 266 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.414 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE HDP0353 | Trademark Plastics Corporation | HDPE | Trademark PE |
| Evermore PUR SW-8021HR | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| HAIPLEN EP10 G3 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Petro Rabigh PE FS250B | Rabigh Refining & Petrochemical Co. | LLDPE | Petro Rabigh PE |
| Monprene® MP-2104 | Teknor Apex Company | TPE | Monprene® |