RTP EMI 461.25 HI FR
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rcIKwY_RTP-EMI-461-25-HI-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. EMI/RFI Shielding - Stainless Steel Fiber 12.5% - High Impact - Flame Retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 46.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 87.8 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257: <1000 ohmSurface Resistivity, ESD S11.11: <100 ohmTensile Elongation, ASTM D638: >10%Volume Resistivity, ASTM D257: <10 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 204 - 246 | °C | |
| Mold Temperature | 65.6 - 82.2 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Remove hopper magnets.Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C HC450 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| ADEKA EPR-4030 | Adeka Corporation | Epoxy | ADEKA |
| ExxonMobil™ LDPE LD 331.08 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Elastollan® 1154 D FHF | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |