Clear Cote™ POLY-U-FOAM™ 2 lb Urethane Foam System
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Club Kit, Inc. |
| Trademark: | Clear Cote™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rbp8Fz_Clear-Cote-POLY-U-FOAM-2-lb-Urethane-Foam-System.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CLEAR COTE™ 2 lb. Urethane Foam System is a high quality Polyol-Isocyanate "foam in place" system with a free raise density of approximately 2 pounds per cubic foot. This system features a convenient easy to use 1 to 1, by volume mix ratio (100 parts A side to 94 parts B side by weight). Product rapidly expands to a rigid closed cell foam perfect for pre-installed pipeline insulation, thermal insulation, acoustic insulation, filling voids, and as sandwich panel core. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Water Absorption | 3.04E-5 | MPa | |
| K (wear) Factor | 0.023 | W/m/K |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Permeability 1 | 1.72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | ASTM D790 | ||
| -- 2 | 0.758 | MPa | |
| -- 3 | 0.731 | MPa | |
| Compressive Modulus | ASTM D1621 | ||
| -- 4 | 5.02 | MPa | |
| -- 5 | 7.14 | MPa | |
| Compressive Strength | ASTM D1621 | ||
| -- 6 | 0.228 | MPa | |
| -- 7 | 0.278 | MPa | |
| Shear Strength | ASTM C273 | ||
| -- 8 | 0.234 | MPa | |
| -- 9 | 0.255 | MPa |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 1.0 | ||
| Part B | Mix Ratio by Volume: 1.0 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 10 | Amber | ||
| -- 11 | Brown | ||
| Density | |||
| -- 12 | 1.17 | g/cm³ | |
| -- 13 | 1.25 | g/cm³ | |
| Viscosity | |||
| -- 14 | 0.30 | Pa·s | |
| -- 15 | 0.50 | Pa·s | |
| Tack Free Time | 6.0 | min |
| Note Message | |
|---|---|
| 1 . | ASTM C355 |
| 2 . | Perpendicular to Rise column |
| 3 . | Parallel to Ride column |
| 4 . | Perpendicular to Rise column |
| 5 . | Parallel to Rise column |
| 6 . | Perpendicular to Rise column |
| 7 . | Parallel to Rise column |
| 8 . | Perpendicular to Rise column |
| 9 . | Parallel to Rise column |
| 10 . | Part B |
| 11 . | Part A |
| 12 . | Part B |
| 13 . | Part A |
| 14 . | Part A |
| 15 . | Part B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® BMC 0170 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| TOTAL Polypropylene PPH 3721WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Braskem PP CP 295 | Braskem | PP Impact Copolymer | Braskem PP |
| LEXAN™ LUX9616G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LG ABS HI121H | LG Chem Ltd. | ABS | LG ABS |