Capilene® T 89 E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rbGLIQ_Capilene-T-89-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® T 89 E is a polypropylene homopolymer intended for fibre applications. CAPILENE ® T 89 E features: anti-gasfading stabilisation, high flow and easy processability. CAPILENE ® T 89 E is suitable for: continuous filaments (CF), bulk continuous filaments (BCF) and fine denier staple fibres; injection molding of household articles, closures, crates and containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 32.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 12 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1450 | MPa | ASTM D790 |
| -- 3 | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256 |
| 23°C | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 97.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® A400MX01 | Toray Resin Company | PPS | Torelina® |
| TUFNYL® SGF 45 GREY | SRF Ltd. | Nylon 6 | TUFNYL® |
| ARC ARC10H | ARC Resin Corporation | Acetal (POM) Homopolymer | ARC |
| LEXAN™ FXE1414T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ STAT-KON™ DE0029EF compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |