AFFINITY™ PL 1881G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ratRAI_AFFINITY-PL-1881G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* PL 1881G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is designed for a variety of demanding packaging applications, including high-speed form-fill-seal products.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.904 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 8.09 | J | Internal method |
| Film Puncture Force (51 µm) | 82.3 | N | Internal method |
| Film Puncture Resistance (51 µm) | 21.9 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 97.4 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 96.9 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 8.07 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 7.17 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 45.4 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 42.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 590 | % | ASTM D882 |
| TD : Fracture, 51 µm | 630 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 830 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 560 | g | ASTM D1922 |
| TD : 51 µm | 730 | g | ASTM D1922 |
| Seal Initiation Temperature 2(51 µm) | 85.0 | °C | Internal method |
| Blocking force | 70 | g | ASTM D3354-89 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 100 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.8 µm) | 112 | ASTM D2457 | |
| Clarity (50.8 µm) | 83.0 | ASTM D1746 | |
| Haze (50.8 µm) | 3.2 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：430°F (221°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：40 rpm |
| Note Message | |
|---|---|
| 1 . | Modified rectangular test piece. |
| 2 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed 10 inches/min (250 mm/s). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1472 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Kumho EP HAG 5220FR | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho EP |
| Karina IVORY PVC COMPOUND 809D35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 5132-75 Clear Pink 6233 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8739-65FU Brown 7349 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |