MEGOLON™ IN700
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rZROrK_MEGOLON-IN700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MEGOLON® IN700 is a thermoplastic, halogen free, fire retardant cable compound which possess excellent insulation properties. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 5.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 1 | 12.5 | MPa | IEC 60811-1-2 |
| -- 2 | 12.0 | MPa | IEC 60811-1-2 |
| -- | 13.0 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Fracture 3 | 160 | % | IEC 60811-1-2 |
| Fracture 4 | 130 | % | IEC 60811-1-2 |
| Fracture | 200 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 9.50 | kN/m | BS 6469 99.1 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air | |||
| 80°C, 168 hr | -4.0 | % | |
| 100°C, 240 hr | -8.0 | % | |
| Change in Tensile Strain at Break in Air | |||
| 80°C, 168 hr | -18 | % | |
| 100°C, 240 hr | -33 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressing Test (90°C) | 20 | % | IEC 60811-3-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | BS 6469 99.2 | ||
| 20°C | 5.0E+14 | ohms·cm | BS 6469 99.2 |
| after 12 hours immersion in water : 20°C | 3.0E+14 | ohms·cm | BS 6469 99.2 |
| after 2 hours immersion in water : 70°C | 1.0E+12 | ohms·cm | BS 6469 99.2 |
| after 2 hours immersion in water : 80°C | 6.0E+11 | ohms·cm | BS 6469 99.2 |
| after 2 hours immersion in water : 90°C | 4.0E+11 | ohms·cm | BS 6469 99.2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Toxicity | 1.10 | NES 713 | |
| Acid gas emission pH | 5.00 | IEC 60754-2 | |
| Acid gas emission conductivity | 10.0 | µS/cm | IEC 60754-2 |
| Smoke Density | ASTM E662 | ||
| Flaming mode 5 | Ds | ASTM E662 | |
| Non-flaming mode 6 | Ds | ASTM E662 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | 0.0 | % | IEC 60754-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 | ||
| Drop down | 1.5:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (10 MHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (10 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 33 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Immersion in salt solution for 10 days at 60°C under continuous 220V electrical stress, UNE 21031-2 Clause 2.5: Pass |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 - 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | after 7 days at 80°C |
| 2 . | after 10 days at 100°C |
| 3 . | after 7 days at 80°C |
| 4 . | after 10 days at 100°C |
| 5 . | Time to maximum: 14 minutes |
| 6 . | Time to maximum: 13 minutes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LS01018 - DP | Premier Polymers, LLC. | LLDPE | Premier |
| PureTherm® 3007C EV5 | Tekni-Films, a div of Tekni-Plex | Film, PE/EVOH/PE/PVC | PureTherm® |
| Carbotex KGN-20MRA | Kotec Corporation | PC | Carbotex |
| Fainplast PVC PM 7010/S | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Electrafil® ABS SS15 BK MB | Techmer Engineered Solutions | ABS | Electrafil® |