GAPEX® RPP20EA34NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rZEV7n_GAPEX-RPP20EA34NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX® RPP20EA34NA is a Polypropylene Homopolymer (PP Homopolymer) material filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Important attributes of GAPEX® RPP20EA34NA are:
Typical application of GAPEX® RPP20EA34NA: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 68.3 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 3630 | MPa | |
| Tangent : 23°C | 3780 | MPa | |
| Flexural Strength (23°C) | 9.65 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 440 | J/m | ASTM D256 |
| Gardner Impact | 0.395 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 154 | °C | |
| 1.8 MPa, Unannealed | 143 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 221 to 238 | °C | |
| Middle Temperature | 227 to 243 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Nozzle Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 221 to 238 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 to 0.345 | MPa | |
| Cushion | 5.08 to 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ C430CF | Mando Advanced Materials Co., Ltd. | LCP | SEPAZ™ |
| Vinylbond 95-950-45 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Hostacom EKC 330N E1 D72806 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| TECACOMP® PA66 CF15 black 4058 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| Durethan® B 31 SK 000000 | LANXESS GmbH | Nylon 6 | Durethan® |