Novalloy-S S6700
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rYwbMS_Novalloy-S-S6700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-S S6700 is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific. Primary attribute of Novalloy-S S6700: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 220°C/10.0 kg | 31 | g/10 min | |
| 240°C/5.0 kg | 21 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 61.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B50 |
| Ball Pressure Test | 90 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 21 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 118 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 2.50 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2500-01A | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Shinko-Lac® ASA TA-15L | Mitsubishi Rayon America Inc. | ASA+PC | Shinko-Lac® |
| Unichem 7342 | Colorite Polymers | PVC, Unspecified | Unichem |
| Hanwha Total PP BJ501X | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| INNOPOL® PP CS 1-3250 | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |