LNP™ FARADEX™ AX88130 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rYimw1_LNPFARADEXAX88130compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* FARADEX* AX88130 is a compound based on ABS resin containing Stainless Steel Fiber. Added feature of this grade is EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound EMI-X PDX-A-88130 Product reorder name: AX88130 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| shrinkage- Flow (23°C, 48 hr) | 0.50 | % | Internal method |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 52.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 - 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 3450 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 160 - 210 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 93.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 200.5 | RTP Company | Nylon 66 | RTP |
| Ultramid® B3ZG6 BK30564 | BASF Corporation | Nylon 6 | Ultramid® |
| Karina WHITE PVC COMPOUD -E 811-10/184-Y-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DEL329XF compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Adsyl 7415 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |