Estane® 58630 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rXbtUo_Estane-58630-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® 58630 is an 82A aromatic Polyether-Based Thermoplastic Polyurethane (TPU). Features: Good physical properties, hydrolysis resistance, low temperature performance and abrasion along with wide processing window for extrusion and low surface tack. Uses: Blown and flat die/cast film extrusion and cable jacketing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 79 - 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 60.0 | mg | ASTM D3389 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (200% Strain) | 15 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain, 0.762mm | 5.20 | MPa | ASTM D412 |
| 300% strain, 0.762mm | 7.60 | MPa | ASTM D412 |
| Tensile Strength (Break, 0.762 mm) | 41.4 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 640 | % | ASTM D412 |
| Tear Strength | |||
| 0.762 mm 1 | 69.6 | kN/m | ASTM D624 |
| Cracking | 23 | kN/m | ASTM D470 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Volume (23°C, 24 hr, in water) | 2.1 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -50.0 | °C | DSC |
| Melting Temperature | 120 | °C | DSC |
| Kofler Melting Temperature | 125 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 166 | °C | |
| Cylinder Zone 2 Temp. | 171 | °C | |
| Cylinder Zone 3 Temp. | 177 | °C | |
| Cylinder Zone 4 Temp. | 182 | °C | |
| Adapter Temperature | 182 | °C | |
| Melt Temperature | 179 | °C | |
| Die Temperature | 182 | °C |
| Extrusion instructions |
|---|
| Dew Point: -40°CScreen Pack Recommendation: 20/40/80 |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 621P | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Staramide RFB53U | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| AKROMID® S3 GF 50 1 natural (3533) | AKRO-PLASTIC GmbH | Nylon 610 | AKROMID® |
| Axiall PVC 19881 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Edgetek™ PC-15CF/000 FCR | PolyOne Corporation | PC | Edgetek™ |