SABIC® PPcompound 7693B
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rWr0Ux_SABIC-PPcompound-7693B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7693B is a very high flow mineral filled modified polypropylene. Material properties include high stiffness and a good impact resistance. SABIC® PPcompound 7693B is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 22.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 16.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 150 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 6.0 | kJ/m² | |
| 0°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 135 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 8.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 HS MS 5 | RTP Company | Nylon 66 | RTP |
| Quadrathane™ ARC-95A-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Andur M-11 (1,4BD) | Anderson Development Company | PUR-Ester/MDI | Andur |
| AXELERON™ CX 6944 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| Innothane® IE-52A | Innovative Polymers, Inc. | TSU-Ether | Innothane® |