Petrotene® PP A3 C35 BRC0001 PH383
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rWGtQF_Petrotene-PP-A3-C35-BRC0001-PH383.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene in white color reinforced with 35% calcium carbonate (CaCO3) for injection molding, combination of stiffness, impact and aesthetics of surface, good set of mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 to 1.8 | % | ASTM D955 |
| Ash Content | 33 to 37 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus | 2460 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 42.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 13.8 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 61.1 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® LB 1901 | Plastic Solutions, Inc. | LLDPE | PrimaFlex® |
| Karina GOLDY BROWN MB (SP31467) -E 36/287-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MACOMASS PP MM-PP GF 20 | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |
| Hifax CA1110 G3 1740 | LyondellBasell Industries | TPO (POE) | Hifax |
| CYCOLAC™ EX39F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |