Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.28 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 155 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 216 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 8.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 to 360 | °C | |
| Middle Temperature | 354 to 371 | °C | |
| Front Temperature | 366 to 385 | °C | |
| Mold Temperature | 93.3 to 163 | °C | |
| Injection Pressure | 68.9 to 124 | MPa | |
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 60 to 90 | rpm | |
| Clamp Tonnage | 6.9 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FLEXCHEM™ 5553 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| GAPEX® RPP10EV02NA | Ferro Corporation | PP, Unspecified | GAPEX® |
| Laser+® C (K62A) | DAK Americas LLC | PET | Laser+® |
| Karina CLEAR PVC COMPOUND -E 80/200-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 65-8961/ES | LEHVOSS Group | PP Copolymer | LUVOCOM® |