Luran® S KR2863C
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Styrolution |
| Trademark: | Luran® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rVYNlQ_Luran-S-KR2863C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran S KR2863C is a blend of ASA and PC providing high impact strength and the highest heat resistance within the product line. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 7.00 | cm³/10min | |
| 260°C/5.0 kg | 18.0 | cm³/10min | |
| Molding Shrinkage | 0.50 to 0.90 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.60 | % | |
| Equilibrium, 23°C, 50% RH | 0.16 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.9 | % | ISO 527-2 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 109 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 130 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 to 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 6.0E-3 | ||
| 1 MHz | 0.010 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Plus Nylon 6 6 | ResMart | Nylon 66 | ResMart Plus |
| Vikalloy IM62 | Viking Polymers, LLC | PMMA+PVC | Vikalloy |
| ALCUDIA® EBA CA-7420B | REPSOL | EBA | ALCUDIA® EBA |
| LEXAN™ HFD1731 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| TECHNYL® C 246SI NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |