DOWLEX™ 2256G
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rUg5z9_DOWLEX-2256G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | |||
| 20 µm | 17.5 | J/cm³ | |
| 51 µm | 9.27 | J/cm³ | |
| Film Toughness | ASTM D882 | ||
| MD : 20 µm | 137 | J/cm³ | |
| MD : 51 µm | 127 | J/cm³ | |
| TD : 20 µm | 126 | J/cm³ | |
| TD : 51 µm | 145 | J/cm³ | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 20 µm | 216 | MPa | |
| 2% Secant, MD : 51 µm | 208 | MPa | |
| 2% Secant, TD : 20 µm | 276 | MPa | |
| 2% Secant, TD : 51 µm | 259 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 11.1 | MPa | |
| MD : Yield, 51 µm | 10.9 | MPa | |
| TD : Yield, 20 µm | 7.86 | MPa | |
| TD : Yield, 51 µm | 11.5 | MPa | |
| MD : Break, 20 µm | 53.6 | MPa | |
| MD : Break, 51 µm | 41.4 | MPa | |
| TD : Break, 20 µm | 41.7 | MPa | |
| TD : Break, 51 µm | 47.5 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 670 | % | |
| MD : Break, 51 µm | 670 | % | |
| TD : Break, 20 µm | 730 | % | |
| TD : Break, 51 µm | 820 | % | |
| Dart Drop Impact | ASTM D1709A | ||
| 20 µm | 200 | g | |
| 51 µm | 330 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 480 | g | |
| MD : 51 µm | 980 | g | |
| TD : 20 µm | 620 | g | |
| TD : 51 µm | 1200 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Melting Temperature | 121 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 20.3 µm | 75 | ||
| 45°, 50.8 µm | 72 | ||
| Haze | ASTM D1003 | ||
| 20.3 µm | 6.3 | % | |
| 50.8 µm | 9.7 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6300HQ | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| ICORENE® 9105 V0 Grey 7005 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| Karina BLACK PVC COMPOUND -E 700-48/1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND 800-48/1-BY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Tunhe PET TH101 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |