Integra™ PC 5020 F1 CL-0001
| Category: | PC , Polycarbonate |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rTunnR_IntegraPC5020F1CL0001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC, High Flow, Mold Release, UV-Stablized, Clear |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2370 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 65.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 110 | % | ASTM D638 |
| Flexural Modulus (50.0 mm Span) | 2310 | MPa | ASTM D790 |
| Flexural Strength (Yield, 50.0 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Peak Load) | 54.2 | J | ASTM D3763 |
| Tensile Impact Strength | 378 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 127 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 - 260 | °C | |
| Middle Temperature | 250 - 275 | °C | |
| Front Temperature | 265 - 290 | °C | |
| Nozzle Temperature | 265 - 300 | °C | |
| Processing (Melt) Temp | 265 - 300 | °C | |
| Mold Temperature | 65 - 105 | °C | |
| Back Pressure | 0.250 - 0.703 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 141 LF Z | RTP Company | PP Homopolymer | RTP |
| Sinvicomp SGH5500G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| INTEGRAL™ 602 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| LNP™ STAT-KON™ KEP33 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Sylvin 8773-60D Grey 9504 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |