Zytel® BM73G15THS BK317
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rSkGmp_Zytel-BM73G15THS-BK317.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 7.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.4 | -- | % | |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5000 | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | 23 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 11 | kJ/m² | |
| 23°C | 21 | 29 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 75 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 21 | 28 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.016 | -- | ||
| 1 MHz | 0.016 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Oxygen Index | 25 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Viscosity (280°C, 1000 sec^-1) | 300 | -- | Pa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 10 SI 2 | RTP Company | Nylon 66 | RTP |
| RTP 4607 | RTP Company | SPS | RTP |
| Reny® 2041 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| FRAGOM PR/6 92 UV NERO | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| SEQUEL® 1820 7C45-UV | LyondellBasell Industries | TPO (POE) | SEQUEL® |