HiFill® PA6 CM40 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rRcuAK_HiFill-PA6-CM40-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA6 CM40 HS is a Polyamide 6 (Nylon 6) product filled with 40% mineral. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.95 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 86.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5720 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 | °C | |
| 1.8 MPa, Unannealed | 119 | °C | |
| CLTE - Flow | 7.2E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 260 to 304 | °C | |
| Processing (Melt) Temp | 243 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Compoceran H901-2 | Arakawa Chemical Industries, Ltd. | PAI | Compoceran |
| Europrene Latice® 440 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Generic Nylon 612 - Glass Bead | Generic | Nylon 612 | Generic |
| LEXAN™ EXL8134 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Crastin® SK609 NC010 | DuPont Performance Polymers | PBT | Crastin® |