ULTEM™ 2300F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rRVYg8_ULTEM-2300F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Water Absorption | |||
| 24 hr | 0.16 | % | ASTM D570 |
| Saturation, 23°C | 0.90 | % | ISO 62 |
| Equilibrium, 23°C | 0.90 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9310 | MPa | ASTM D638 |
| -- | 9500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 169 | MPa | ASTM D638 |
| Yield | 165 | MPa | ISO 527-2/5 |
| Break 3 | 159 | MPa | ASTM D638 |
| Break | 165 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 5 | 3.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 8950 | MPa | ASTM D790 |
| -- 7 | 8500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 225 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 225 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 10 | 40 | kJ/m² | ISO 180/1A |
| 23°C 11 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 490 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 212 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 210 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 12 | 210 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 228 | °C | ASTM D1525 13 |
| -- | 213 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -20 to 150°C | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 25 | kV/mm | |
| 1.60 mm, in Oil | 30 | kV/mm | |
| Dielectric Constant (1 kHz) | 3.70 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.5E-3 | ||
| 2.45 GHz | 5.3E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 50 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP323M | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| NEFTEKHIM PE 2062U (62111) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| ALTECH® PP-H A 4920/107 MR20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Kemcor LD 1434 | Qenos Pty Ltd | LDPE | Kemcor |
| Karina PINK PVC COMPOUND 852-39/156-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |