ASTATAL™ FG2010
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTATAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rRTFnb_ASTATAL-FG2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTATAL™ FG2010 is a 10% chemically coupled glass fibre filled (GF) Polyoxymethylene (POM or Polyacetal) copolymer designed for use in automotive fuel component mouldings. Note: The letters "U" or "W" indicate additional UV stabilisation [ ie:ASTATAL™ FG2010U ]. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 89.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 4000 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 158 | °C | |
| Melting Temperature | 165 | °C | DSC |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 165 to 185 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 185 to 205 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR LX5 02-15 | TOTAL Refining & Chemicals | PP Copolymer | TOTAL Polypropylene |
| ACCUTECH™ CP0437G5M25CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| EXCEVAL™ RS-2817SB | Kuraray Co., Ltd. | EVA | EXCEVAL™ |
| Generic PS+PE | Generic | PS+PE | Generic |
| Petrothene® NA345 | LyondellBasell Industries | LDPE | Petrothene® |