OP - PC - Unfilled 912-FDA
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Unfilled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rQzOM7_OP---PC---Unfilled-912-FDA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP-PC-Unfilled 912-FDA is a polycarbonate (PC) material,. This product is available in North America and is processed by injection molding. The main features of OP-PC-Unfilled 912-FDA are:
OP-PC-Unfilled 912-FDA's typical application areas are: food contact applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 68.9 | MPa | ASTM D638 |
| Flexural Modulus | 2310 | MPa | ASTM D790 |
| Flexural Strength | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 800 | J/m | ASTM D256 |
| Dart Drop Impact | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 129 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-2 | UL 94 | |
| 3.18 mm | V-2 | UL 94 |
| Additional Information |
|---|
| Melt Mass - Flow Rate (MFR), ASTM D1238, 300°C/1.2kg: 9 to 13 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 - 124 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 271 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silamid® M15 | Roonamid a.s. | Nylon 6 | Silamid® |
| Bergamid™ B70 G15 H TM-Z UV SO6 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| EPLAMID 6 GFT 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| LNP™ LUBRICOMP™ DCP36 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Hifax CB 1160 G1 C11538 | LyondellBasell Industries | PP Copolymer | Hifax |