Quadrant EPP Symalit ECTFE
| Category: | ECTFE , Ethylene Chlorotrifluoroethylene Copolymer |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rQtK28_Quadrant-EPP-Symalit-ECTFE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Symalit ECTFE is an Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) product. It can be processed by extrusion and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.010 | % | |
| Saturation | 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 48.3 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | 34.5 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.7 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 149 | °C | |
| Peak Crystallization Temperature (DSC) | 240 | °C | ASTM D3418 |
| CLTE - Flow 1(-40 to 149°C) | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 3 | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 68°F |
| 2 . | EOS/ESD S11.11 |
| 3 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® 540TC NAT | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Geon™ Vinyl Flexible R235AE White 1875 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Elastron® G G400.A05.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Hylex® P1025L | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| RONFALIN® ABS 1363 | A. Schulman Europe | ABS | RONFALIN® |