STYRON A-TECH™ 1175
| Category: | PS (HIPS) , Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rQmaWa_STYRON-A-TECH-1175.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A-TECH™ 1175 advanced technology polystyrene is a high impact, environmental stress crack resistant (ESCR) resin, designed for extrusion and thermoforming applications, especially for the refrigeration industry. Based on patented technology, this resin allows for potential downgauging and scrap reduction in the thermoforming process through its combination of properties like ESCR, rigidity and thermoforming. Main characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.8 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 16.0 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain (Break) | 60 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 1650 | MPa | ISO 178 |
| Flexural Stress 3 | 38.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1A |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 8.2 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 68.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/A120 |
| -- | 89.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 4(1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Granulation 7 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ FFX100 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| ULTEM™ 4002 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Gallonprene® GP540-8001(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ENFLEX EA3555A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Petlon Prime B1-G30-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |