Ebalta BLH 200 / W 15
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rQXk9V_Ebalta-BLH-200-W-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Slight discoleration of the hardener by oxygen possible, which doesn't affect the products quality. Demoulding of laminates made at room temperature (20°C) is possible. The parts show very good strength. To achieve maximum property values for example for flexural strength and heat resistance, we recommend thermal treatment at the recommended temperature. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.12 to 0.14 | % | |
| Saturation, 23°C 1 | 0.32 to 0.36 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 to 82 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3630 to 3930 | MPa | ISO 527-2 |
| Tensile Stress | 69.0 to 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.8 to 9.2 | % | ISO 527-2 |
| Flexural Modulus | 2160 to 2460 | MPa | ISO 178 |
| Flexural Stress | 98.0 to 118 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 81.0 to 85.0 | °C | TMA |
| Martens Temperature | 64 to 68 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 30 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 50°C | 12 to 15 | hr | |
| 80°C | 12 to 15 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Viscosity (25°C) | 0.39 to 0.55 | Pa·s | |
| Curing Time (20°C) | 8.0 to 10 | hr | |
| Pot Life | |||
| 23°C 2 | 12 to 15 | min | |
| 20°C 3 | 14 to 16 | min |
| Note Message | |
|---|---|
| 1 . | 168 h |
| 2 . | 500 g |
| 3 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CompaDur® 121 GK 30 natural (009) | DimeLika Plast GmbH | PBT | CompaDur® |
| Ferro PP LPP25BC64NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hostacom M4 U42 LW92607 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| TABOREN® PC 73 T 20-074 | SILON s.r.o. | PP Copolymer | TABOREN® |
| Sylvin 6177-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |