Ultradur® B 4330 G6 HR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rPI0Sz_Ultradur-B-4330-G6-HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection-moulding grade containing 30% glass-fibres, for rigid,tough and dimensionally stable technical parts, used in applications with highest demands on hydrolysis resistance such es automotive connectors and housings for electronic units under the hood. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 108 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2 |
| Flexural Modulus | 7860 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 65 | kJ/m² | |
| 23°C | 74 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 2.0E-5 to 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Maximum Service Temperature - short cycle operation | 210 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 250 | mm/sec |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 255 | °C | |
| Front Temperature | 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 AR 10 TFE 15 | RTP Company | PPS | RTP |
| TEKNIFLEX® VPA15200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| DOW™ HDPE DMDA-8940 HEALTH+™ | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Europrene® SOL T 6434 | Versalis S.p.A. | SBS | Europrene® |
| Globalene® PJ3004 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |