Plexiglas® DR-100G
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rObESf_Plexiglas-DR-100G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® DR-100G is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications. This grade is formulated for approved medical applications. It is a heat resistant resin with minimal edge color and provides 10 times the impact resistance of standard acrylics. It is an all-acrylic resin that combines the toughness associated with other impact plastics and the outstanding transparency and UV resistance of conventional acrylic materials. Moldflow simulation data is available. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 45 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 88.9 | °C | |
| 1.8 MPa, Annealed | 79.4 | °C | |
| Vicat Softening Temperature | |||
| -- | 97.8 | °C | ASTM D1525 2 |
| -- | 86.1 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 90.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 2.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0231V1 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PolyFR™ 201 | JJI Technologies, LLC | PE, Unspecified | PolyFR™ |
| SWANCOR Epoxy 900 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Novodur® E211 | Styrolution | ABS | Novodur® |
| Ferro PP TPO20AT19GY | Ferro Corporation | PP, Unspecified | Ferro PP |
| LNP™ FARADEX™ MS003 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ FARADEX™ |