Moplen HP420M
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rOHKs5_Moplen-HP420M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP420M is a high flow polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP) on tubular double bubble lines and cast film. Typical applications are BOPP packaging, laminating film and drinking straws but also packaging foodstuffs such as pasta, snacks, biscuits, bakery products and confectionery, film for packaging for flowers, books stationery, blankets, shirts, knitwear and hosiery. For regulatory information please refer to Moplen HP420M Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 33.0 | MPa | |
| Break | 21.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 12 | % | |
| Break | > 500 | % | |
| Flexural Modulus | 1350 | MPa | ISO 178 |
| Coefficient of Friction (Dynamic, Cast Film) | > 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elastic Modulus - MD 1(50 µm, Cast Film) | 800 | MPa | Internal Method |
| Elastic Modulus - TD 2(50 µm, Cast Film) | 800 | MPa | Internal Method |
| Tensile Strength 3 | ASTM D882 | ||
| MD : Break, 50 µm, Cast Film | 50.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 45.0 | MPa | |
| Tensile Elongation 4 | ASTM D882 | ||
| MD : Break, 50 µm, Cast Film | 950 | % | |
| TD : Break, 50 µm, Cast Film | 1000 | % | |
| Dart Drop Impact 5 | 250 | g | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 153 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 6(45°, Cast Film) | 91 | Internal Method | |
| Haze 7(50.0 µm, Cast Film) | 3.8 | % | Internal Method |
| Note Message | |
|---|---|
| 1 . | MA 18068 |
| 2 . | MA 18068 |
| 3 . | 500 mm/min |
| 4 . | 500 mm/min |
| 5 . | MA17106 |
| 6 . | MA 17021 |
| 7 . | MA 17031 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net XP 9400 | Polytech & Net Gmbh | mLLDPE | Polytech & Net |
| Witcom POM-C 5M-RDT | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| HIVAL® 5108 | Nexeo Solutions, LLC. | PS (GPPS) | HIVAL® |
| Karina NATURAL PVC COMPOUND 800-25/1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ ML008 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ LUBRICOMP™ |