INEOS LLDPE LL8109AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rNb6nZ_INEOS-LLDPE-LL8109AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LLDPE for Blown film LL8109AA has been developed for use in rich blends for mulch film, refuse sacks, liners and other thin film applications where excellent mechanical performance is required. Characteristics LL8109AA is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL8109AA. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% secant, MD : 25 µm, blown film | 175 | MPa | ISO 1184 |
| 1% secant, TD : 25 µm, blown film | 195 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : 25 µm, blown film | 60.0 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 25 µm, blown film | 590 | % | ISO 1184 |
| TD : Broken, 25 µm, blown film | 750 | % | ISO 1184 |
| Dart Drop Impact (25 µm, Blown Film) | 300 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.0 µm | 137.3 | kN/m | ASTM D1922 |
| TD : 25.0 µm | 251.1 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 41 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 25 µm film, 2.5:1 blow up ratio, 200°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell GA7760 | LyondellBasell Industries | HDPE | Purell |
| Sylvin 2819-80 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| TOTAL Polypropylene PPH 10012 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| AIE PC 10G6 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| EnviroPro 1020GF45 | West Michigan Compounding | PP Copolymer | EnviroPro |