TRIREX® 3030U
| Category: | PC , Polycarbonate |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rNWiUe_TRIREX-3030U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRIREX® 3030U is a Polycarbonate (PC) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 70.1 | MPa | |
| -- | 70.6 | MPa | |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 2290 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 92.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 1000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 134 | °C | ASTM D648 |
| CLTE - Flow | 5.0E-5 to 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 260 | °C | |
| Middle Temperature | 250 to 275 | °C | |
| Front Temperature | 265 to 290 | °C | |
| Nozzle Temperature | 265 to 300 | °C | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 65.0 to 105 | °C | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.020 to 0.80 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 7054 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Sumitomo Silicone SI 9045C | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| Varcum 29538 | Durez Corporation | Phenolic | Varcum |
| Chiao Fu PA66 MD312G43 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| LNP™ THERMOCOMP™ RX12402 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |