LNP™ LUBRILOY™ D2000P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rLE6hW_LNP-LUBRILOY-D2000P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing, Wear Resistant. Also known as: LNP* LUBRILOY* Compound D-EP Product reorder name: D2000P |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.81 | % | ISO 294-4 |
| Flow : 24 hr | 0.84 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1930 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 56.4 | MPa | ASTM D638 |
| Yield | 54.3 | MPa | ISO 527-2 |
| Break | 46.4 | MPa | ASTM D638 |
| Break | 46.1 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.9 | % | ASTM D638 |
| Yield | 5.3 | % | ISO 527-2 |
| Break | 42 | % | ASTM D638 |
| Break | 43 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2280 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 86.7 | MPa | ASTM D790 |
| -- | 86.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.19 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor - Washer | 44.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 40.3 | J | ASTM D3763 |
| -- | 43.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 131 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 304 to 316 | °C | |
| Processing (Melt) Temp | 304 to 316 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP ERTALON® 66 SA | Quadrant Engineering Plastic Products | Nylon 66 | Quadrant EPP |
| Sup-tech A9705P | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| NITRIFLEX N-7920 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| Techsil® RTV27905 | Techsil Limited | Silicone Rubber, RTV-2 | Techsil® |
| NORYL™ WCD841U resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |