TRANSMARE® 14CT30-0.001
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rL8uLU_TRANSMARE-14CT30-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CT30-0.001 is a 30% fine, white talc filled polypropylene copolymer for injection molding purposes with high impact and good flow. Suitable for light colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 10 | g/10 min | |
| 230°C/5.0 kg | 45 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 21.0 | MPa | |
| Break, 4.00 mm | 16.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 2.5 | % | |
| Break, 4.00 mm | 24 | % | |
| Flexural Modulus 1 | 2750 | MPa | ISO 178 |
| Flexural Stress 2 | 34.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 2.4 | kJ/m² | |
| -20°C | 2.5 | kJ/m² | |
| 0°C | 3.5 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 2.7 | kJ/m² | |
| -20°C | 3.2 | kJ/m² | |
| 0°C | 4.5 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® MA 4411 | Arkema | Nylon 12 | Rilsan® |
| TAROBLEND 50 X0 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| Electrafil® PA6/6 05002 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Oleflex™ 6261-70A-8843 Black, 307105 | Vi-Chem Corporation | TPE | Oleflex™ |
| Sylvin 802-85 CLEAR BLUE 841 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |