PROTEQ™ C28T2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rKyga7_PROTEQ-C28T2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PROTEQ™ C28T2 is a high flow 10% Talc filled grade of polypropylene copolymer. It is intended for use in applications where a balance of flow and rigidity is required. Note: The letter U in the product name indicates that UV stabiliser has been added (PROTEQ™ C28UT2) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw D | 69 | ISO 868 | |
| Shaw D, 15 seconds | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1800 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 38.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 60 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 125 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 60.0 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 195 - 215 | °C | |
| Middle Temperature | 205 - 225 | °C | |
| Front Temperature | 215 - 235 | °C | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 4040 G10 | BASF Corporation | PBT+PET | Ultradur® |
| NYCOA Polyamide 4230 HST | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Evermore PUR SS-143G | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Hipolyene 8015 FRC | Zylog Plastalloys | TPO (POE) | Hipolyene |
| LEXAN™ 241S resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |