Horda E6595
| Category: | PE Copolymer , Polyethylene Copolymer |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rKO1Fp_Horda-E6595.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
E6595 is a crosslinkable semiconductive compound, based on ethylene copolymer compound, designed for conductor screen and insulation shield applications in XLPE and EPDM rubber insulated cables with bonded shield.E6595 have:
E6595 meets the requirements as below, when optimal processing extrusion and end testing procedure are used:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 27 | MU | ISO 289 |
| Moisture 1 | ppm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 2(200°C) | 30 - 40 | % | IEC 540 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 15.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 220 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | -5.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (135°C, 168 hr) | -20 | % | ASTM D573 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 1.0E+2 | ohms·cm | ASTM D257 |
| 90°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 60.0 | °C | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Cylinder Zone 1 Temp. | 80.0 - 120 | °C | |
| Cylinder Zone 2 Temp. | 80.0 - 120 | °C | |
| Cylinder Zone 3 Temp. | 80.0 - 120 | °C | |
| Cylinder Zone 4 Temp. | 80.0 - 120 | °C | |
| Cylinder Zone 5 Temp. | 80.0 - 120 | °C | |
| Die Temperature | 100 - 125 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 125°CHead Temperature: 100 to 125°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WINTEC™ WFW4M | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| ADMER™ AT2018A | Mitsui Chemicals America, Inc. | PE, Unspecified | ADMER™ |
| Grilamid® LV-3A H | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Karina MBU RED E 42/404-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOTUF™ DF004PSI compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOTUF™ |