ACRYLITE® MD™ H12
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® MD™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rKLRWY_ACRYLITE-MD-H12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® MD™ H12 acrylic polymer is an amorphous thermoplastic molding compound based on polymethyl methacrylate (PMMA) for the medical diagnostic industry. Typical properties of ACRYLITE® MD™ acrylic polymers are:
The special properties of ACRYLITE® MD™ H12 polymer are:
Application: Used for injection molding of medical devices requiring UV spectroscopy for fluid evaluation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 to 6.0 | % | |
| Break | 4.0 to 6.0 | % | |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 93.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| CLTE - Flow (0 to 156°C) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 1.0 | % | ASTM D1003 |
| Yellowness Index (3.20 mm) | < 1.0 | YI | ASTM D1925 |
| UV Transmittance 1(3.20 mm) | > 88 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Wavelength: 340 nm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P IR D-30 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Vinnolit® VK 710 | Vinnolit GmbH & Co. KG | PVC Alloy | Vinnolit® |
| Xuchuan XCBD-200 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Kingfa JH710 G10D | Kingfa | PC Alloy | Kingfa |
| Kumho EPS SEPS N20 HC | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |