Dow Corning® C6-530

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Dow Corning®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rHb9l4_DowCorningC6530.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Liquid Silicone Rubber for device and component fabrication in the healthcare industry APPLICATIONS DOW CORNING Class VI Elastomers (C6-530, C6-540, C6-550, C6-560, C6-570) Parts A & B are platinum-catalyzed materials designed for part fabrication and medical devices, including those intended for implantation in humans for up to 29 days. DESCRIPTION DOW CORNING Class VI Elastomers (C6-530, C6-540, C6-550, C6-560, C6-570) Parts A & B are a series of two-part platinum-catalyzed silicone elastomers. Each elastomer is supplied as a two-part kit (Part A and Part B), equal portions of which must be thoroughly blended together prior to use. The elastomer is thermally cured via an addition-cure (platinum-catalyzed) reaction. When blended and cured as indicated, the resulting elastomer consists of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica. The elastomers are available in a range of nominal hardness from 30 to 70, Durometer-Shore A. The elastomers can be used without any post-cure although if necessary, this may be employed to stabilize final properties. Furthermore, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

Liquid Silicone Rubber for device and component fabrication in the healthcare industry

APPLICATIONS
DOW CORNING Class VI Elastomers (C6-530, C6-540, C6-550, C6-560, C6-570) Parts A & B are platinum-catalyzed materials designed for part fabrication and medical devices, including those intended for implantation in humans for up to 29 days.

DESCRIPTION
DOW CORNING Class VI Elastomers (C6-530, C6-540, C6-550, C6-560, C6-570) Parts A & B are a series of two-part platinum-catalyzed silicone elastomers. Each elastomer is supplied as a two-part kit (Part A and Part B), equal portions of which must be thoroughly blended together prior to use. The elastomer is thermally cured via an addition-cure (platinum-catalyzed) reaction. When blended and cured as indicated, the resulting elastomer consists of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica. The elastomers are available in a range of nominal hardness from 30 to 70, Durometer-Shore A. The elastomers can be used without any post-cure although if necessary, this may be employed to stabilize final properties. Furthermore, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability No frost Workability, good Fast curing Good coloring High pressure heating resistance
Uses	Medical/nursing supplies
Agency Ratings	EP Unspecified Rating ISO 10993-Part I USP Class VI

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.13	g/cm³	ASTM D792
Molding Shrinkage - Flow	2.0	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	30		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	0.890	MPa	ASTM D412
Tensile Strength	8.20	MPa	ASTM D412
Tensile Elongation (Break)	830	%	ASTM D412
Tear Strength ¹	27.5	kN/m	ASTM D624

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
Radilon® AGV 20 Black	Radici Plastics	Nylon 66	Radilon®
RheTech Thermoplastic Polyolefin FT2500-00	RheTech, Inc.	Polyolefin, Unspecified	RheTech Thermoplastic Polyolefin
STERLENE™ KB010-A4001	R&P (Pte.) Ltd.	PP Homopolymer	STERLENE™
Karina BLACK PVC COMPOUND 753-48/ 1-C-IS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
TECHNYL® C 216 V45 BLACK 34N	Solvay Engineering Plastics	Nylon 6	TECHNYL®