TEKALOY™ T80HI
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rHD4A6_TEKALOY-T80HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEKALOY™ T80HI is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.70 | % | |
| Across Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 44.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 58.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 610 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 112 | °C | |
| 1.8 MPa, Unannealed | 89.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3499-3 X 91193 A | RTP Company | LCP | RTP |
| MIRASON™ F312 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| ACCUTECH™ HP0339W40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| APEX® 86-K264A-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| MAJORIS DFR111R | AD majoris | PP, Unspecified | MAJORIS |