| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LOXIM Industries Private Limited |
| Trademark: | LOXIM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rH6ZaS_LOXIM-820-02C-HB.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| LOXIM 820 02C HB is a Polypropylene product filled with 20% calcium carbonate. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 to 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 to 1.7 | % | ASTM D1299 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 25.0 to 27.0 | MPa | ASTM D638 |
| Flexural Modulus | 1500 to 1700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 to 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 105 to 110 | °C | ASTM D648B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 383A2R30009 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| TRIMID® N6-200N | Polymer Technology and Services, LLC | Nylon 6 | TRIMID® |
| Genestar™ N1006D-H31 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Karina COMP. PVC GRAY -E 680D18/664-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |
| Shida 026 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |