Rilsan® BMNO P20 TLD
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rGWBPq_Rilsan-BMNO-P20-TLD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BMNO P20 TLD is a polyamide 11 produced from a renewable source. This natural grade is plasticized and for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 1.1 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 68 | ||
| Shore D, 15 sec | 61 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 545 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 30 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 420 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 186 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11-P, MHLR, 12-005 | ISO 1874 | |
| Renewable Carbon Conent | > 92 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 210 to 280 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 880 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| TEKNIFLEX® PXPO103 | Tekni-Films, a div of Tekni-Plex | Film, Copolyester/PE/EVOH/PE | TEKNIFLEX® |
| Spartech Polycom SCR7F-7010A | Spartech Polycom | PC | Spartech |
| TRIREX® Compound HF3000HG10 | Samyang Corporation | PC | TRIREX® Compound |
| LUVOCOM® 1-8259 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |