Ultrason® P 3010 NAT
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rGVk6a_Ultrason-P-3010-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, medium viscosity injection moulding grade, flameretardent and with improved chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.90 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % | |
| Viscosity Number 1 | 71.0 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 124 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2270 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 74.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 7.8 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 198 | °C | ISO 75-2/A |
| Glass Transition Temperature 2 | 220 | °C | ISO 11357-2 |
| CLTE - Flow | |||
| 23 to 80°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| 180°C | 6.3E-5 | cm/cm/°C | DIN 53752 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 44 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.7E-3 | ||
| 1 MHz | 8.9E-3 | ||
| Comparative Tracking Index (Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 350 | °C | |
| Middle Temperature | 360 | °C | |
| Front Temperature | 370 | °C | |
| Nozzle Temperature | 370 | °C | |
| Processing (Melt) Temp | 350 to 390 | °C | |
| Mold Temperature | 140 to 180 | °C | |
| Screw Speed | < 300 | mm/sec |
| Note Message | |
|---|---|
| 1 . | in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tritan™ EX401 | Eastman Chemical Company | Copolyester | Tritan™ |
| Xuchuan XCUR-M9500 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| KPOL-PP K-PHC 18.0 B | KPOL Chem Co. | PP Copolymer | KPOL-PP |
| LNP™ VERTON™ RV00AES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| PLUSTEK PA320G3 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |